温度湿度适宜,开始加强
大蜥蜴终于等到了适合的温度湿度,环氧和玻纤布加强一波,太难刷了,300G环氧下去,希望永远不要爆壳子,挺有意思和颜值的双发cathttp://image.rcfans.com/pic/20220414/1649915861573703_827.jpg?x-oss-process=image/watermark,image_cGljLzIwMjExMDA2L29zc18xNjMzNTM0ODIxOTgzXzg2NF81MzNfNTYucG5n,t_50,g_se,x_20,y_20
http://image.rcfans.com/pic/20220414/164991586157820_27.jpg?x-oss-process=image/watermark,image_cGljLzIwMjExMDA2L29zc18xNjMzNTM0ODIxOTgzXzg2NF81MzNfNTYucG5n,t_50,g_se,x_20,y_20
http://image.rcfans.com/pic/20220414/1649915861797740_672.jpg?x-oss-process=image/watermark,image_cGljLzIwMjExMDA2L29zc18xNjMzNTM0ODIxOTgzXzg2NF81MzNfNTYucG5n,t_50,g_se,x_20,y_20
http://image.rcfans.com/pic/20220414/1649915861876112_156.jpg?x-oss-process=image/watermark,image_cGljLzIwMjExMDA2L29zc18xNjMzNTM0ODIxOTgzXzg2NF81MzNfNTYucG5n,t_50,g_se,x_20,y_20
http://image.rcfans.com/pic/20220414/1649915861954114_240.jpg?x-oss-process=image/watermark,image_cGljLzIwMjExMDA2L29zc18xNjMzNTM0ODIxOTgzXzg2NF81MzNfNTYucG5n,t_50,g_se,x_20,y_20
http://image.rcfans.com/pic/20220414/1649915862155657_817.jpg?x-oss-process=image/watermark,image_cGljLzIwMjExMDA2L29zc18xNjMzNTM0ODIxOTgzXzg2NF81MzNfNTYucG5n,t_50,g_se,x_20,y_20
很专业,https://app.rcfans.com/public/emotion/face_jizhi.pnghttps://app.rcfans.com/public/emotion/face_jizhi.pnghttps://app.rcfans.com/public/emotion/face_jizhi.pnghttps://app.rcfans.com/public/emotion/face_jizhi.png 看工艺原壳应该是不饱和树脂的你这样加环氧可能会分层 最好能抽个真空,要不然很不均匀。 ztony 发表于 2022-04-14 21:43
最好能抽个真空,要不然很不均匀。
真空在这样的船内是实现不了的原装都不是真空的样子 专业,很专业 jery 发表于 2022-04-14 22:17
真空在这样的船内是实现不了的原装都不是真空的样子
倒也是,不过原装应该是抽真空之后再合模。 ztony 发表于 2022-04-15 19:18
倒也是,不过原装应该是抽真空之后再合模。
不饱和树脂用不了抽真空要是做环氧碳纤维壳这船就贵了去了 看着原厂也挺结实啊,这船还分新款老款吗 个人意见,选碳纤维或凯夫挂混纺,相对结实,如再有疑问,可考虑用金属,目前有做不锈钢的,我就搞了条鱼雷艇,当然竞速艇也可以的,只要有图纸。是真结实,曾高速撞到石阶,除了掉漆,别的没事。就是重量偏重,个人在找有无用铝合金材质造船的大师,那重量与结实程度均可有保障。